Reinforcing Bars. Reinforcing steel shall be clean and free from loose mill scales, dust, loose rust and coats of paints, oil, grease or other coating, which may impair or reduce bond. Reinforcing bars should be : 1. TMT steel (Thermo Mechanically Treated), Grade Fe 500, high strength deformed steel bars conforming to IS: 1786, IS :456, latest revision. 2. The TMT bars should have Yield strength 500Mpa, Tensile Strength 580MPA and Elongation in % 20. 3. Hard‑drawn steel wire fabric conforming to IS: 1566, IS 456 ‑ latest revision. All steel reinforcement above 6mm diameter shall necessarily be of tested quality. Test of each batch of reinforcement shall be carried out in an approved laboratory at the Contractor's cost to show the acceptability of the material. Along with all types strength test of the reinforcement bars, the Contractor shall conduct bend/re-bend test, as well.
Appears in 3 contracts
Sources: Contract Agreement, Procurement Agreement, Contract Agreement
Reinforcing Bars. Reinforcing steel shall be clean and free from loose mill scales, dust, loose rust and coats of paints, oil, grease or other coating, which may impair or reduce bond. Reinforcing bars should be :
1. TMT steel (Thermo Mechanically Treated), Grade Fe 500, high strength deformed steel bars conforming to IS: 1786, IS :456, latest revision.
2. The TMT bars should have Yield strength 500Mpa, Tensile Strength 580MPA and Elongation in % 20.
3. Hard‑drawn Hard-drawn steel wire fabric conforming to IS: 1566, IS 456 ‑ - latest revision. All steel reinforcement above 6mm diameter shall necessarily be of tested quality. Test of each batch of reinforcement shall be carried out in an approved laboratory at the Contractor's cost to show the acceptability of the material. Along with all types strength test of the reinforcement bars, the Contractor shall conduct bend/re-bend test, as well.